SABIC沙伯基础创新Lexan PC 940物性表
以下是SABIC沙伯基础创新Lexan PC 940中英文物性表资料
SABIC Innovative Plastics Lexan® 940 PC
特性：阻燃V0，防火
Material Notes:
LEXAN 940 is a medium viscosity flame retardant grade, especially suitable for electrical applications.
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium吸湿平衡
0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption吸水率 at Saturation
0.35 %
@Temperature 23.0 °C
0.35 %
@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow熔体流动速率
9.0 g/10 min
@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min
@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Hardness, H358/30
95.0 MPa
13800 psi
ISO 2039-1
Tensile Strength at Break断裂拉伸强度
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield屈服拉伸强度
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break断裂伸长率
85 %
85 %
50 mm/min; ISO 527
Elongation at Yield屈服伸长率
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus弯曲弹性模量
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)
12.0 kJ/m²
@Temperature -30.0 °C
5.71 ft-lb/in²
@Temperature -22.0 °F
80*10*3; ISO 180/1A
70.0 kJ/m²
@Temperature 23.0 °C
33.3 ft-lb/in²
@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
80*10*3; ISO 180/1U
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched 夏比缺口试样冲击
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击
1.40 J/cm²
@Temperature -30.0 °C
6.66 ft-lb/in²
@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.00 J/cm²
@Temperature 23.0 °C
14.3 ft-lb/in²
@Temperature 73.4 °F
ISO 179/2C
7.30 J/cm²
@Temperature 23.0 °C
34.7 ft-lb/in²
@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
10
@Load 1.00 kg
10
@Load 2.20 lb
CS-17; SABIC Method
Electrical Properties电性能
Metric公制数据
English英制数据
Comments测试方法
Volume ResiSTivity体积电阻率
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance表面电阻
>= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant介电常数
2.7
@Frequency 1.00e+6 Hz
2.7
@Frequency 1.00e+6 Hz
IEC 60250
2.7
@Frequency 50.0 - 60.0 Hz
2.7
@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength介电强度
17.0 kV/mm
@Thickness 1.00 mm
432 kV/in
@Thickness 0.0394 in
short time; IEC 60243-1
17.0 kV/mm
@Thickness 3.20 mm
432 kV/in
@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor耗散因数
0.0010
@Frequency 50.0 - 60.0 Hz
0.0010
@Frequency 50.0 - 60.0 Hz
IEC 60250
0.010
@Frequency 1.00e+6 Hz
0.010
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index跟踪指数
225 V
225 V
IEC 60112
Thermal Properties热性能
Metric公制数据
English英制数据
Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数
70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity导热系数
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test热球压力测试
<= 140 °C
<= 284 °F
IEC 60695-10-2
Deflection Temperature at热变形温度0.46 MPa (66 psi)
136 °C
277 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at热变形温度1.8 MPa (264 psi)
125 °C
257 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point维卡软化点
141 °C
286 °F
Rate B/50; ISO 306
142 °C
288 °F
Rate B/120; ISO 306
150 °C
302 °F
Rate A/50; ISO 306
UL RTI, Electrical相对温度指数
130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact机械冲击热指数
120 °C
248 °F
UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数
125 °C
257 °F
UL 746B
Flammability, UL94阻燃等级
V-0
@Thickness 1.10 mm
V-0
@Thickness 0.0433 in
UL 94
Oxygen Index氧指数
35 %
35 %
LOI; ISO 4589
Glow Wire Test灼热丝测试
825 °C
@Thickness 1.00 mm
1520 °F
@Thickness 0.0394 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
850 °C
@Thickness 2.00 mm
1560 °F
@Thickness 0.0787 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
850 °C
@Thickness 1.00 mm
1560 °F
@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C
@Thickness 1.60 mm
1760 °F
@Thickness 0.0630 in
Glow Wire Flammability Index; IEC 60695-2-12