Zytel® ST801 NC010

NYLON RESIN

DuPont Performance Polymers

产品说明:

Unreinforced, Super Toughened, Polyamide 66

物性信息:

基本信息
添加剂
  • 脱模

RoHS 合规性
  • 联系制造商

形式
  • 粒子

加工方法
  • 薄膜挤出

  • 挤出

  • 浇铸

  • 片材挤出成型

  • 涂层

  • 型材挤出成型

  • 注射成型

多点数据
  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

部件标识代码 (ISO 11469)
  • >PA66-HI

树脂ID (ISO 1043)
  • PA66-HI

物理性能干燥调节后的单位制测试方法
密度1.07--g/cm³ISO 1183
收缩率


ISO 294-4
     横向流量1.4--%ISO 294-4
     流量1.8--%ISO 294-4
吸水率 (23°C, 24 hr)1.1--%ISO 62
机械性能干燥调节后的单位制测试方法
拉伸模量2000900MPaISO 527-2
拉伸应力 (50% 应变)49.044.0MPaISO 527-2
拉伸应变 (断裂)> 50> 50%ISO 527-2
拉伸蠕变模量


ISO 899-1
     1 hr--800MPaISO 899-1
     1000 hr--700MPaISO 899-1
弯曲模量1800700MPaISO 178
冲击性能干燥调节后的单位制测试方法
简支梁缺口冲击强度


ISO 179/1eA
     -30°C2020kJ/m²ISO 179/1eA
     23°C, 局部断裂70100kJ/m²ISO 179/1eA
悬壁梁缺口冲击强度


ISO 180/1A
     -40°C2017kJ/m²ISO 180/1A
     -30°C1515kJ/m²ISO 180/1A
     23°C8090kJ/m²ISO 180/1A

Characteristics of DuPont PA66 plastic raw materials in the United States:


1. It has excellent wear resistance, self-lubrication, and high mechanical strength. However, due to its high water absorption, its dimensional stability is poor


2. PA66 can maintain strong strength and stiffness at higher temperatures. PA66 still has hygroscopicity after molding, and its degree mainly depends on the material composition, wall thickness, and environmental conditions.


3. When designing products, it is important to consider the impact of moisture absorption on geometric stability. In order to improve the mechanical properties of PA66, various modifiers are often added. Glass is the most common additive, and sometimes synthetic rubber such as EPDM and SBR are added to improve impact resistance. PA66 has low viscosity, therefore it has good fluidity (but not as good as PA6). This property can be used to process very thin components. Its viscosity is very sensitive to temperature changes.


4. The shrinkage rate of PA66 ranges from 1% to 2%, and adding glass fiber additives can reduce the shrinkage rate to 0.2% to 1%. The difference in shrinkage rate between the process direction and the direction perpendicular to the process direction is significant. PA66 has solubility resistance to many solvents, but has weak resistance to acids and other chlorinating agents.